| IT-71T-1 |
| Classification |
Average composition of
deposit |
Application |
diameter
mm |
AWS A 5.20 : E71T1MH4
EN 758: T42 2 P M1H5 |
| C% |
0.06 |
| Mn% |
1.30 |
| Si% |
0.45 |
| S% |
< 0.025 |
| P% |
< 0.025 |
|
Rutile flux-cored wire,
suitable for all position welding of carbon steels.
Shielding gas: Ar/Co2 e Co2. |
1.20
1.60 |
| IT-70T-5 |
| Classification |
Average composition of
deposit |
Application |
diameter
mm |
AWS A 5.20 : E70T5(M)H4
EN 758: T42 4 B C M4H5 |
| C% |
0.07 |
| Mn% |
1.60 |
| Si% |
0.55 |
| S% |
< 0.025 |
| P% |
< 0.025 |
|
Basic flux-cored
wire - suitable for all position welding, except
vertical down, of high grade carbon steels.
Good Mechanical values, also at low temperature.
Shielding gas: Ar/Co2 e Co2.
|
1.20
1.60 |
| IT-MSG350 |
| Classification |
Average composition of
deposit |
Application |
diameter
mm |
MSG1-350
DIN 8555 : 1-350 |
| C% |
0.24 |
| Mn% |
1.50 |
| Si% |
0.60 |
| Cr% |
1.60 |
| S% |
< 0.025 |
| P% |
< 0.025 |
|
Flux.cored wire for
hard-facing with hardness values HB 320-370.Suitable
for hard-facing on rolls, wheels, etc... |
1.20
1.60 |
| IT-MSG660 |
| Classification |
Average composition of
deposit |
Application |
diameter
mm |
| DIN 8555 : MSG6-60 |
| C% |
0.50 |
| Mn% |
1.50 |
| Si% |
0.60 |
| Cr% |
5.50 |
| Mo% |
0.60 |
| S% |
< 0.025 |
| P% |
< 0.025 |
|
Flux-cored wire hard-facing
with hardness values HRC 52-57. Excellent impact strength.
Suitable for the rebuilding of oil-presses, agricultural
machines - only tool-workable. |
1.20
1.60 |
|